Cold Applied Tape

Shandong Xunda Anticorrosion Coating Co.,Ltd is a China cold applied tape manufacturer, supplier and company, our professional factory can provide you cold applied tape products with both good price and quality.

Tape coating for pipeline anticorrosion tape

System description:

LDPE cold applied tape for underground pipeline is used as the base material which is coated by the liquid butyl rubber film, both of which are pressed and compounded. LDPE cold applied tape will protect the pipe and its anti-corrosion tape surface from pipeline damages. Xunda LDPE cold applied tape have been specially developed for high-quality, corrosion protection for joints, in cases where the pipeline has already been installed. The material is easy, safe and quick to apply on welded joints, bends and other complicated shapes.

Structure:

The coating & wrapping system as defined by this specification is a Three Part System, made up to the following parts for either hand or machine application:

2.1.1 TAPE-INNER:

This part consists of two components:

i) Adhesive:Inner layer of butyl rubber.

ii) Backing: Outer layer of Polyethylene (PE) plastic.

2.1.2 TAPE-OUTER:

This part consists of two components as in inner wrap tape i.e.

i) Adhesive:Inner layer of butyl rubber.

ii) Backing :Outer layer of Polyethylene (PE) plastic. 

2.1.3 PRIMER: 

A viscous liquid of petroleum spirit base compatible with the above Inner and Outer Wraps applied directly on pipes. 

Features & Benefits

3.1 Tape Inner Wrap

3.1.1 The inner wrap tape shall be two ply plastic tape consisting of stabilized polyethylene (PE) base of outer layer (backing) with a layer of butyl rubber (adhesive) applied on one side. 

3.1.2 The thickness of plastic base shall not be less than 13mils. Thickness of butyl rubber shall not be less than 12 mils. The total thickness of the tape shall not be less than 25 mils. 

3.1.3The inner wrap tape must be compatible with the properties of the primer and the properties of outer wrap tape.

3.1.4PE backing colour shall be black.

3.2 TAPE-OUTER WRAP:

3.2.1 The Outer Wrap Tape shall be two-ply plastic tape consisting of stabilized polyethylene base of outer layer (backing) with a layer of butyl rubber (adhesive) applied on one side.

3.2.2 The thickness of the butyl rubber layer shall not be less than 5 mils. The total thickness of the tape shall not be less than 25 mils. 

3.2.3 PE backing colour shall be White.

3.3 PRIMER:

The primer shall consist of butyl rubber and unsaponifiable resins in petroleum spirit and it shall be compatible with the butyl adhesive that is furnished on the inner wrap tapes, must be free flowing, and have the ability to cover voids, pits and welds. The primer must provide an acceptable base for butyl adhesive on the tapes.

Physical Properties

ITEM OF SPECIFICATIONS

TEST METHOD

VALUE

Inner Wrap

Outer Wrap

Total thickness (mils)

ASTM  D 1000

≥25

≥25

PE  backing (mils)

-do-

≥13

≥20

Butyl Rubber adhesive (mils)

-do-

≥12

≥5

Tensile strength at +23oC 

(N/10 mm tape width)

-do-

≥50

≥50

Yields strength at +23oC 

(N/10 mm tape width)

-do-

≥40

≥40

Elongation at break at +23oC

-do-

≥200%&≤400%

≥200%&≤400%

Adhesion to primed steel at +23oC

at 300 mm/min. rate of extension

(N/10 mm tape width)

-do-

≥25

-

Water vapor transmission rate

(Gm/M2/24hrs)

ASTM E 96

≤ 0.2

≤ 0.1

Water absorption at +23oC after 1 day

ASTM D 570

≤ 0.1%

≤ 0.1%

Dielectric strength 

(KV/mm Thickness)

ASTM D 1000/ ASTM D 145  

≥ 40

≥ 40

Application temperature 

-

5oC  to  50oC

5oC  to  50oC

Colour

-

Black

White